Product Name: Flexible Polyimide Foam
Item No.: SolverPI-Flexible Foam
Since 2010, based on the original technology and refer ourself to the international technical standard, SOLVER POLYIMIDE developed a new type of flexible PI foam integrated production line has been built,with1000MT annual output. With different needs,we can produce the PIfoam of density and intensity.The PIfoam has the characters of high and low heat resistence,High fire retardent,radiation resistence,wave-transparent,microwave absorpting,anti-corrosion,longlife,excellent comprehensive properties,the high rate of obturator,easy processing. It can be widely used in aviation, spaceflight, navigation, transportation, construction and so on.
This product has past the fire retardancy test in the Yuandong fire experiment center.And the result show that our material is in well accordance with the technique target of smoke density、toxicity test、low flame-spread combuston heat value in《International fire test program application rules》require.The room temperature emissions、high temperature split product、inhalation toxicity experiments on animals are in accordance with human bddy health standards after Non metallic material inspection center of People’s Liberation Army Navy detection.
1.Surface:The surface should be smooth,the form hole be well-distributed.
2.Qualty:Product quality and conditions should be consistent,clean,no impurities and defects affecting the processing or material properties.
3.Color:The original color unless special provision.
4.Toxicity:Avirulent,no harm to the skin long-term exposure.
6.Thickness:Based on the order,the error±5％ is permitted.
Table 1 the specification of flexible PI foam
Flexible PI foam
GB/T 6343 The determination of apparent density of foam and rubber.
GB/T10295 The determination of insulation material of thermal,heat flow meter method.
96hThe moisure absorption rate(relative humidity95％，temperature 49℃±2℃)
GB/T20312 The determination of consruction material and the products’hygrothermal performance,moisure absorption performance
There is not marked change apparent when radiation dose attain 10000Gy.
JJF1018We use the potassium bichromate(silver)dose to measure the ray water uptake dose
No crack,-35℃ Not sticky,150℃,12h
GB/T9640Flexible and rigid foam polymer materials,accelerated aging test
Acid resistence(20％hydrochloric acid)
There is not change in surface after steeped for 24h.
Alkali resistence(10％ caustic soda)
There is not any change in surface after steeped for 24h.
There is not any change in volum after steeped for 24h.
GB/T6344Flexible foam polymer materials,the determination of tensile srength and crack growth rate
GB/T6669Flexible foam polymeric materials Determiniation of compression set
Toxicity of material
Ordinary temperatures toxicity
Meet the requirement of GJB 11.2、GJB 11.3 rules.
GJB11BNuclear submarine cabin air composition allowable concetration requirements.
GJB3881Toxicity assessment of nonmetallic materials for ship.
Oridinary temperatures smoke and toxicity
Meet the requirement of FTP’s rules
IMO 2010FTP Part2 of rule The smoke and toxicity testing procedures
Fire protecting performance
GB/T2406.2 Determination of the burning behaviour of plastics by oxygen index method.Part 2 greenhouse experiment.
Density of smoke(Dm)
(Flameless mode flame mode)
GB/T10671 Test method for specific optical density of smoke generated by solid materials
After leaving the fire ignited material 1s self extinguishing and no droplet
GB/T2408 Test method for flammability of plastics.Level method and vertical method
Low flame spread
Meet the requirement of FTP
IMO2010FTP The rule part 5-The surface materials flammability testing procedures
Heat of combustion,MJ/ m2
ISO1716The determination of heat of combustion
The construction technology
No dust,easyto cut,easy packaging,construction technology can meet the requirements of the users.
Noise reduction cofficient
GB/T18696.1 The measurement of the acoustic impdance of sound absorption coefficient and impedance in tube Part1:Voltage Standing Wave Ratio
The concentration of harmful gases does not exceed the requirements of GJB 11B provisions of the cabin air froup divided allowable concetration.The material of the median lethal concentration LC50≥50g/m3.
According to the 2010FTP rules of Annex 1 second part2--The smoke and toxicity testing procedures under the condition of high temperature and smoke density detection materials smoke toxicity.The average optical density ratio requirement of flue gas(Dm) ≤200;The smoke toxicity concentration was less than the limit value in table 2.
Table 2 The limit value of toxics smoke concentration(Unit:ppm)
Note:SO2 for floor coverings,this index is 200ppm
According to the 2010FTP rules of Annex 1 second part 5--Material testing for pocedures for combusion,See Table 3 for specific requirements.
Table 3 PI foam surface burning characteristics
Surface combustion characteristic index
Go out when the critical heat flux,kW/ m2
Continuous combustion heat,MJ/ m2
Gross heat release,MJ
The heat release peak,Kw
Storage:The material must be stored in damp-proof packing and keep dry,the packing meet the need of military standard.
Lable the message in the corner of every panel as follow:
1、Material standard number,type,specification.
2、Lot No.and date of producted.
4、Logo of company.
5、Order No.(out packing only)
6、Quantity of load(out packing only)